Aluminium profile
1. High quality material and well finished
2. High corrosion resistance
3. easy to operate and maintain
electrophrestic aluminium champagne from Shandong
| Profile | Building profiles | Industrial profiles |
| State | 6060, 6061, 6063, 7005 | |
| temper | T5, T6 | |
| Colors | Silver, cream, white, blue, red, champagne, simulated stainless steel, sand, bronze, black, etc. | |
| Surface treatment | Mill finish, matted, sandblast, anodizing, electrophoretic coating, powder coating, thermal break, wooden grain | |
| Hardness | 8-14HW | |
| Mould | Based on your drawing or use our mould free | |
| thickness | Minimum 0.8mm for profile; 10-20um for oxidation film; 40-120um for powder coat | |
| Usages | Windows, doors, curtain wall, solar panel, LED panel, heat sink, etc. | |
| Certified | ISO9001-2008, ISO14001, SONCAP, GB5237-2008( equals to BS, AAMA, JISH) | |
Chemical composition
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Impurity | Al |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.90 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
| 6061 | 0.4-0.8 | 0.70 | 0.15-0.40 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | 0.15 | Rest |
| 6005 | 0.6-0.9 | 0.35 | <0.1 | <0.1 | 0.40-0.6 | <0.1 | <0.1 | <0.1 | <0.15 | Rest |
Mechanical property
| Alloy | Condition | Tensile strength | Yield strength | Elongation | Vickers hardness |
| 6061 | T6 | >265Mpa | >245Mpa | >8% |
|
| 6063 | T5 | >160Mpa | >110Mpa | >8% | HV>58 HW>8 |
| T6 | >205Mpa | >180Mpa | >8% |
|
Colored anodized profile
| Grade | Thickness of film | Hole scaling quality of oxide layer | |
| Average thickness | Local thickness | P. Cr acid-erosion weight less method | |
| AA10 | >10um | >8mm | <30 mg/d m 2 |
| AA15 | >15um | >12um | |
Electrophoretic coating profiles
| Grade | Anodic oxide film | Thickness of paint film | Thickness of complex film | Film hardness | |
| Average thickness | Local thickness | ||||
| A | >10um | >8um | >12um | >21um | >3um |
| B | >10um | >8um | >7um | >17um | >3um |
Powder coating & wooden-grained profile
| Coating thickness | Coating impress rigidity | Adhesive force of coating layer |
| 40-120um | Indentation hardness>80 | 0 grade |
Thermal-break profile
| type | Characteristic value of longitudinal shear strength Tc | Characteristic value of transverse strength Qc |
| Inserting | >24N/mm | >24N/mm |
| Pouring | >24N/mm | >24N/mm |
| Place of Origin: |
Shandong China (Mainland)
|
Grade: |
6000 Series
|
Temper: |
T3-T8
|
| Application: |
Door & Window
|
Shape: |
as per detailed drawing
|
Alloy Or Not: |
Is Alloy
|
| Model Number: |
as per drawing item no.
|
Brand Name: |
Ruilihua
|