| ≥1 piece |
LDPE HDPE LLDPE Virgin Recycled
Color: available
Lead Time: 2-3 weeks
Sample: available
Origin: South Africa
CAS No.9002-88-4
Formula: [CH2CH2]n
EINECS 200-842-0Application for injection moulding, film, blow gradeLDPE HDPE LLDPE GRANULAR HDPE PELLET
Specific properties:
film grade
|
Item |
Test condition |
Test Method |
Value |
Unit |
|
Density |
|
ISO 1183 |
0.944-0.955 |
g/cm3 |
|
MFR |
190°C/2.16kg |
ISO 1133 |
0.03-0.07 |
g/10min |
|
Tensile strength at yield |
|
ISO 527-2 |
22 |
MPa |
|
Elongation at break |
|
ISO 527-2 |
>350 |
% |
|
ESCR |
F50, 50°C, 100% |
ASTM D-1693A |
1000 |
h |
|
VICAT |
|
ASTM D-1525 |
126 |
°C |
blown grade
|
Item |
Test Condition |
Test Method |
Value |
Unit |
|
Density |
|
ISO 1183 |
0.950~0.955 |
g/cm |
|
MFR |
190°C/2.16kg |
ISO 1133 |
1.7~2.5 |
g/10min |
|
Tensile strength at yield |
|
ISO 527-2 |
24 |
MPa |
|
Elongation at break |
|
ISO 527-2 |
>600 |
% |
injection grade
|
Item |
Test Condition |
Test Method |
Value |
Unit |
|
MFR |
190°C/2.16kg |
ASTM D-1238 |
20 |
g/10min |
|
Density |
--- |
ASTM D-792 |
0.954 |
g/cm3 |
|
Tensile strength at yiled |
--- |
ASTM D-638 |
28 |
MPa |
|
Elongation at break |
--- |
ASTM D-638 |
250 |
% |
|
Impact tensile strength |
--- |
ASTM D-1822 |
42 |
kJ/m2 |
|
ESCR |
|
ASTM D-1693 |
3 |
--- |
|
VACIT |
--- |
ASTM D-1525 |
127 |
°C |
HDPE (high density PE) - is used in products and packaging such as plastic bags, Milk jugs, detergent bottles, Margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.