2014 hot selling HDPE/LDPE/LLDPE/PP plastic raw materials 1,All kinds of LLDPE
2,LLDPE high quality with good price
3,big sto
2014 hot selling HDPE/LDPE/LLDPE/PP plastic raw materials
High Quality LLDPE Virgin/Recycled Granules
1, LLDPE film grade
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 2.0±0.4 | g/10min |
| Density | 920±2 | Kg/cm3 |
| Tensile Strengthat Yield | 8 | Mpa ≥ |
| Tensile Strengthat Break | 12 | Mpa ≥ |
| haze | 15 | %≤ |
| Packing | In 25 kg PP woven bags,20MT/20’FCL | |
2, LLDPE for Master Batch Use
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 20 | g/10min |
| Density | 0.924 | g/cm 3 |
| Tensile Strength | MD12 | Mpa |
| TD 10 | ||
| Elongation at Yield | 13 | % |
| Elongation at Break | 200 | |
| Dark Drop Impact | 105 | g |
| Brittle Temperature(F 50) | -70 | °C |
| Vicat Softening Point | 90 | °C |
| Packing | In 25 kg PP woven bags,20MT/20’FCL | |
3, LLDPE Powder Rotational Molding Grade for Tank Use
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 3.2 | g/10min |
| Density | 0.939 | g/cm 3 |
| Melting Point | 127 | °C |
| Tensile Yield Strength | 21 | Mpa |
| Tensile Strength at Break | 28 | Mpa |
| Elongation at Break | 1,100 | % |
| Flexural Modulus | 750 | Mpa |
| Brittle Temperature | <-60 | °C |
| Place of Origin: |
Zhejiang China (Mainland)
|
Brand Name: |
Sinopec, Saudi Arabia, samsung
|
Model Number: |
1002KW 118W 118N 118Z
|
| colour: |
white red black blue
|
grade: |
virgin recycled
|