Various color engineering plastic POM plate
Description
POM is a kind of engineering plastic with good mechanical properties. POM together with UHMW PE, Nylon, PTFE are known as four most abrasion resistant plastics. It has almost the same rigidity as metal, so it's an ideal replacement material of copper, cast zinc, steel, aluminum and other metal materials. We are able to produce POM products without bubbles or cracks.
Characteristics
-High surface hardness
-Good wear resistance
-Excellent machinability
-Nice self-lubricating properties
-Good dimensional stability
-Low water absorption
-Oil resistant
-Work under the temperature of -40-100 centidegrees
Applications
Bearings
POM bearings own excellent stability and good wear resistance in various kinds of moist environments.
Gears
POM has high stiffness and rigidity, good self-lubricating properties. So it has taken the place of metal gears in many applications. (Prior materials: Bronze, Stainless Steel)
Rollers
Guide rollers machined from POM rod operate smoothly and reliably in lift gate systems used to load cargo onto truck beds. (Prior materials: Cast Iron, Cast Aluminium)
Structural Keels
With excellent fatigue and impact resistance, POM is a suitable material of continuously loaded structural keel for prosthetic device. (Prior materials: Nylon, PU)
Slide Blocks
Low coefficient friction, wear resistant, self-lubricating, no need for lubricating oil.
Technical Data Sheet
| PROPERTIES | Test Method | Unit | Value |
| I.Physical Properties | |||
| Density | ISO 1183 | g/cm3 | 1.45 |
| Water absorption 24hrs | ISO 62 | % | < 0.3 |
| II.Thermal Properties | |||
| Heat deflection temperature - HDT/A | ISO 75A | ºC | 110 |
| Min. service temperature | ºC | -40 | |
| Max. service temperature | ºC | 100 | |
| Thermal conductivity at 23 ºC | DIN 11359 | W/(K*m) | 0.31 |
| Coefficient of linear thermal expansion | ISO 11359 | 10-4*K-1 | 1.2 |
| Flammability Rating(6mm thickness) | UL 94 | - | HB |
| III.Mechanical Properties at 23ºC | |||
| Tensile strength at yield | ISO 527-2 | MPa | 63 |
| Tensile strength at break | ISO 527-2 | Mpa | - |
| Elongation at break | ISO 527-2 | % | 31 |
| Modulus of elasticity after tensile test | ISO 527-2 | MPa | 2,700 |
| Modulus of elasticity after flexural test | ISO 178 | MPa | - |
| Hardness - Shore D | DIN 53505 | 83 | |
| Charpy impact strength | ISO 179 | kJ/m2 | N. B. |
| Friction coefficient | DIN 53375 | 0.35 | |
| IV.Electrical Properties at 23ºC | |||
| Dielectric constant at 1 MHz | IEC 60250 | 106Hz | 3.8 |
| Dielectric loss factor at 1 MHz | IEC 60250 | 106Hz | 0.005 |
| Volume resistively | IEC 60093 | Ohm (Ω) * cm | >1013 |
| Surface resisively | IEC 60093 | Ohm (Ω) | >1013 |
| Dielectric strength | IEC 60243-1 | kV/mm | 40 |
| NOTE: 1 g/cm3 = 1,000 kg/m3, 1 Mpa = 1 N/mm2, 1kV/mm = 1 MV/m | |||
| Statement: | |||
| Property data contained herein are typical values of resin for your reference and comparison purposes only. PRIOR will not provide any legally binding guarantee of certain properties, or any suitability. | |||